Cievka z nehrdzavejúcej ocele 410S
Popis
Technické údaje:
1. Štandard: ASTM A240, JIS G4304, EN10088
2. Stupeň: 200séria&300séria&400séria
3. Hrúbka: 0,03 mm - 6,0 mm
4. Šírka: 8mm-600mm
5. Dĺžka: podľa požiadavky zákazníkov
6. Povrch: 2D, 2B, BA, zrkadlová úprava, N04, vlasová línia, matný povrch, 6K, 8K
7.Technológia: ťahané za studena/valcované za studena/valcované za tepla
Materiály:
| Typ | stupeň | stupeň | Chemická zložka % | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | Iné | |||
| austenitické | 201 | SUS201 | ≤0,15 | 16:00-18:00 | 3,50-5,50 | 5,50 – 7,50 | ≤0,060 | ≤0,030 | - | ≤1,00 | - | ≤0,25 | - |
| 202 | SUS202 | ≤0,15 | 17:00-19:00 | 4:00-6:00 | 7,50-10,00 | ≤0,060 | ≤0,030 | ≤1,00 | - | ≤0,25 | - | ||
| 301 | 1,4310 | ≤0,15 | 16:00-18:00 | 6:00-8:00 | ≤ 2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | ≤0,10 | - | |
| 304 | 1,4301 | ≤0,07 | 17:00-19:00 | 8:00-10:00 | ≤ 2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 304 l | 1,4307 | ≤0,030 | 18:00-20:00 | 8:00-10:00 | ≤ 2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 304H | 1,4948 | 0,04-0,10 | 18:00-20:00 | 8:00-10:00 | ≤ 2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 309 | 1,4828 | ≤0,20 | 22:00-24:00 | 12:00-15:00 | ≤ 2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 309S | * | ≤0,08 | 22:00-24:00 | 12:00-15:00 | ≤ 2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 310 | 1,4842 | ≤0,25 | 24:00-26:00 | 19:00-22:00 | ≤ 2,00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 310S | * | ≤0,08 | 24:00-26:00 | 19:00-22:00 | ≤ 2,00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 314 | 1,4841 | ≤0,25 | 23:00-26:00 | 19:00-22:00 | ≤ 2,00 | ≤0,045 | ≤0,030 | - | 1,50-3,00 | - | - | - | |
| 316 | 1,4401 | ≤0,08 | 16:00-18:50 | 10:00-14:00 | ≤ 2,00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1,00 | - | - | - | |
| 316L | 1,4404 | ≤0,030 | 16:00-18:00 | 10:00-14:00 | ≤ 2,00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1,00 | - | - | - | |
| 316Ti | 1,4571 | ≤0,08 | 16:00-18:00 | 10:00-14:00 | ≤ 2,00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1,00 | - | 0,1 | Ti5(C+N)~0,70 | |
| 317 | * | ≤0,08 | 18:00-20:00 | 11:00-15:00 | ≤ 2,00 | ≤0,045 | ≤0,030 | 3:00-4:00 | ≤1,00 | - | 0,1 | - | |
| 317L | 1,4438 | ≤0,03 | 18:00-20:00 | 11:00-15:00 | ≤ 2,00 | ≤0,045 | ≤0,030 | 3:00-4:00 | ≤1,00 | - | 0,1 | - | |
| 321 | 1,4541 | ≤0,08 | 17:00-19:00 | 9:00-12:00 | ≤ 2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Ti5(C+N)~0,70 | |
| 321H | * | 0,04-0,10 | 17:00-19:00 | 9:00-12:00 | ≤ 2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Ti5(C+N)~0,70 | |
| 347 | 1,4550 | ≤0,08 | 17:00-19:00 | 9:00-12:00 | ≤ 2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Nb>10*C%-1,10 | |
| 347H | 1,494 | 0,04-0,10 | 17:00-19:00 | 9:00-12:00 | ≤ 2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Nb>10*C%-1,10 | |
| Duplex | 2205 | S32205 | ≤0,03 | 22,0-23,0 | 4,5-6,5 | ≤ 2,00 | ≤0,030 | ≤0,020 | 3,0-3,5 | ≤1,00 | - | 0,14-0,20 | |
| 2507 | S32750 | ≤0,03 | 24,0-26,0 | 6,0-8,0 | ≤1,20 | ≤0,035 | ≤0,020 | 3,0-5,0 | ≤0,80 | 0,5 | 0,24-0,32 | ||
| Ferit | 409 | S40900 | ≤0,03 | 10,50-11,70 | 0,5 | ≤1,00 | ≤0,040 | ≤0,020 | - | ≤1,00 | - | ≤0,030 | Ti6(C+N)~0,50 Nb:0,17 |
| 430 | 1Cr17 | ≤0,12 | 16:00-18:00 | - | ≤1,0 | ≤0,040 | ≤0,030 | - | ≤1,0 | - | - | - | |
| 444 | S44400 | ≤0,025 | 17:50-19:50 | 1 | ≤1,00 | ≤0,040 | ≤0,030 | 1,75-2,5 | ≤1,00 | - | 0,035 | Ti+Nb:0,2+4(C+N)~0,80 | |
| Martenzit | 410 | 1Cr13 | 0,08-0,15 | 11.50-13.50 | 0,75 | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - |
| 410S | * | ≤0,080 | 11.50-13.50 | 0,6 | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 420 | 2Cr13 | ≥0,15 | 12:00-14:00 | - | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 420J2 | 3Cr13 | 0,26-0,35 | 12:00-14:00 | - | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - | |
| PH | 630 | 17-4 PH | ≤0,07 | 15:00-17:50 | 3.00-5.00 | ≤1,00 | ≤0,035 | ≤0,030 | - | ≤1,00 | 3.00-5.00 | - | Nb 0,15-0,45 |
| 631 | 17-7 PH | ≤0,09 | 16:00-18:00 | 6,50-7,50 | ≤1,00 | ≤0,035 | ≤0,030 | - | ≤1,00 | ≤0,50 | - | Al 0,75-1,50 | |
| 632 | 15-5 PH | ≤0,09 | 14:00-16:00 | 3,50-5,50 | ≤1,00 | ≤0,040 | ≤0,030 | 2.00-3.00 | ≤1,00 | 2,5-4,5 | - | Al 0,75-1,50 | |
Základné informácie
Cievka z nehrdzavejúcej ocele 410s, s dobrou odolnosťou proti korózii a obrobiteľnosťou, je to oceľ na všeobecné použitie a oceľ na rezné nástroje.410S je druh ocele, ktorá môže zlepšiť odolnosť proti korózii a tvárnosť ocele 410. 410S je oceľ s vysokou pevnosťou, ktorá môže ďalej zlepšiť odolnosť ocele 410 proti korózii.Používa sa na lopatky turbín a diely s vysokou teplotou.
• Špecifikácie: AISI 410s, ASTM 410s
• Povrchové úpravy: Ba povrch, 2b povrch, No.1 (biela koža), 2D povrch, No.4 (matný), HL (drôtkovanie), 8K povrch majú vynikajúcu kvalitu povrchu
• Platia tolerancie frézovania na hrúbku a rovinnosť. Ak potrebujete špecifické veľkosti alebo smer zrna, zavolajte JM Steel.
410S Charakteristická technológia obrábania
1D - Povrch má nespojitý zrnitý tvar, známy tiež ako hmlová plocha.
Technológia spracovania: valcovanie za tepla + žíhanie brokovaním morenie + valcovanie za studena + morenie žíhaním.
2D - Mierne strieborná biela farba.
Technológia spracovania: valcovanie za tepla + žíhanie brokovaním morenie + valcovanie za studena + morenie žíhaním.
2B -- Strieborná biela s lepším leskom a rovinnosťou ako 2D povrch.
Technológia spracovania: valcovanie za tepla + žíhanie brokovaním morenie + valcovanie za studena + žíhanie morenie + kalenie a popúšťanie.
Ba - Vynikajúci povrchový lesk, vysoká odrazivosť, ako zrkadlový povrch.
Technológia spracovania: valcovanie za tepla + žíhanie brokovaním morenie + valcovanie za studena + žíhanie morenie + leštenie povrchu + kalenie a popúšťanie valcovaním.
č. 3 -- Dobrý lesk, hrubozrnný povrch.
Technológia spracovania: leštenie a popúšťanie valcovaním pre 2D alebo 2B so 100~120 abrazívnymi materiálmi (JIS R6002).
č.4 -- Dobrý lesk, jemné línie na povrchu.
Proces spracovania: leštenie a temperovanie valcovaním pre 2D alebo 2B s 150 ~ 180 abrazívnymi materiálmi (JIS R6002).
HL -- Strieborne sivá s pramienkami vlasov.
Technológia spracovania: 2D produkty alebo 2B produkty s vhodnou zrnitosťou brúsnych materiálov na leštenie povrchu je súvislé brúsne zrno.
MIRRO -- Zrkadlové.
Technológia spracovania: 2D produkty alebo 2B produkty s vhodnou zrnitosťou brúsneho materiálu brúsením a leštením do zrkadlového efektu.